腐蝕抑制劑對Fe-Co-Ni-Cu-Al高熵合金在3.5%NaCl水溶液中之抑制效應
|
| 並列篇名 |
Effects of Corrosion Inhibitors on the Fe-Co-Ni-Cu-Al High Entropy Alloy in 3.5% NaCl Solution. |
| 作者 |
葉威德、陳柏洲、開物、吳建國 |
| 中文摘要 |
本研究主要探討三種腐蝕抑制劑對FeCoNiCuAl高熵合金在3.5%NaCl水溶液中的抑制行為。由電化學實驗結果得知，三種抑制劑中、添加Na3PO4將使高熵合金的孔蝕電位值（Ep i t）最高且鈍化區（△ E p）範圍最大，NaNO2次之，而Na2MoO4最小；同時，鈍化電流密度（ip a s s）則以NaPO4最小，Na2MoO4次之，NaNO2最大，顯示添加Na3PO4對高熵合金的腐蝕抑制效果最好。 |
| 英文摘要 |
This study is to evaluate the corrosion resistance of the newly developed Fe-Co-Ni-Cu-Al high entropy alloy (HEA) in 3.5% NaCl solutions. Three corrosion inhibitors(Na3PO4 Na2MoO4and NaNO2 ) were chosen to improve the corrosion resistance in test solutions. The results indicated that Na3PO4 exhibited the best corrosion inhibition efficiency among the test inhibitors due to improving the passivity region and reducing the passivation current in polarization curves. |
| 起訖頁 |
273-280 |
| 關鍵詞 |
腐蝕抑制劑、高熵合金（FeCoNiCuAl）、鈍化、Corrosion inhibitors、High entropy alloy (HEA)、Passivity |